两个基于2,5-二甲氧基对苯二甲酸和咪唑衍生物的超分子钴配位聚合物的结构及光催化反应

本文以咪唑衍生物为配体,通过水热合成法与钴离子制备出两个配位聚合物:{[Co(DTA)(1,4-DIB)(H₂O)]·H₂O}_n(1)和[Co(DTA)(1,3-BMIB)]_n(2)(1,4-DIB=1,4-二(1H-咪唑-1-基)苯; 1,3-BMIB=1,3-二(4-甲基-1H-咪唑-1-基)苯;H₂DTA=2,5-二甲氧基对苯二甲酸)。利用X射线单晶衍射、粉末衍射、热失重、元素分析、红外光谱以及固体紫外-可见光谱等对两个配合物进行了表征。结构分析证实配合物1和2是通过二维结构堆积成的三维超分子化合物。粉末衍射测试则显示两个配合物在水中有很好的稳定性。固体紫外-可见光谱显示两个配合物属半导体材料,对紫外-可见光有很强的吸收作用。在光催化实验中,配合物1和2可加快亚甲基蓝的降解速度。     

Insights into the efficient charge separation over Nb2O5/2D-C3N4 heterostructure for exceptional visible-light driven H2 evolution

Two-dimensional carbon nitride(2 D-C₃ N₄)nanosheets are promising materials in photocatalytic water splitting,but still suffer from easy agglomeration and fast photogene rated electron-hole pairs recombination.To tackle this issue,herein,a hierarchical Nb₂ O₅/2 D-C₃ N₄ heterostructure is precisely constructed and the built-in electric field between Nb₂O₅ and 2 D-C₃ N₄ can provide the driving force to separate/transfer the charge carriers efficiently.Moreover,the strongly Lewis acidic Nb₂O₅ can adsorb TEOA molecules on its surface at locally high concentrations to facilitate the oxidation reaction kinetics under irradiation,resulting in efficient photogene rated electrons-holes separation and exceptional photocatalytic hydrogen evolution.As expected,the champion Nb₂O₅/2 D-C₃N₄ heterostructure achieves an exceptional H2 evolution rate of 31.6 mmol g^-1 h^-1,which is 213.6 times and 4.3 times higher than that of pristine Nb₂O₅ and2 D-C₃N₄,respectively.Moreover,the champion heterostructure possesses a high apparent quantum efficiency(AQE)of 45.08%atλ=405 nm and superior cycling stability.Furthermore,a possible photocatalytic mechanism of the energy band alignment at the hetero-interface is proposed based on the systematical characterizations accompanied by density functional theory(DFT)calculations.This work paves the way for the precise construction of a high-quality heterostructured photocatalyst with efficient charge separation to boost hydrogen production.     

Interface engineering of porous Fe2P-WO2.92 catalyst with oxygen vacancies for highly active and stable large-current oxygen evolution and overall water splitting

Constructing a low cost,and high-efficiency oxygen evolution reaction(OER)electrocatalyst is of great significance for improving the performance of alkaline electrolyzer,which is still suffering from highenergy consumption.Herein,we created a porous iron phosphide and tungsten oxide self-supporting electrocatalyst with oxygen-containing vacancies on foam nickel(Fe₂P-WO_2.92/NF)through a facile insitu growth,etching and phosphating strategies.The sequence-controllable strategy will not only generate oxygen vacancies and improve the charge transfer between Fe₂P and WO_2.92 components,but also improve the catalyst porosity and expose more active sites.Electrochemical studies illustrate that the Fe₂P-WO_2.92/NF catalyst presents good OER activity with a low overpotential of 267 mV at 100 mA cm^-2,a small Tafel slope of 46.3 mV dec^-1,high electrical conductivity,and reliable stability at high current density(100 mA cm^-2 for over 60 h in 1.0 M KOH solution).Most significantly,the operating cell voltage of Fe₂P-WO_2.92/NF‖Pt/C is as low as 1.90 V at 400 mA cm^-2 in alkaline condition,which is one of the lowest reported in the literature.The electrocatalytic mechanism shows that the oxygen vacancies and the synergy between Fe₂P and WO_2.92 can adjust the electronic structure and provide more reaction sites,thereby synergistically increasing OER activity.This work provides a feasible strategy to fabricate high-efficiency and stable non-noble metal OER electrocatalysts on the engineering interface.     

基于2,5-二溴对苯二甲酸配体的锌/钴配合物合成、晶体结构及性质

将有机物2,5-二溴对苯二甲酸(H₂L₁)和2,2′-联吡啶(L₂)作为双配体,使用溶剂热法和七水合硫酸锌(ZnSO₄·7H₂O)、六水合硝酸钴(Co(NO₃)₂·6H₂O)分别反应,得到配合物[Zn(L₁)(L₂)(H₂O)]_n(1)和配合物[Co(L₁)(L₂)(H₂O)]_n(2)。采用单晶X射线衍射、元素分析、红外光谱、紫外光谱、荧光光谱、热重分析等测试方法对这两种物质进行分析研究。单晶测试结果表明配合物1是单斜晶系,以Zn²⁺配位连接L^2-₁与L₂形成一维链状结构,各条链在分子间氢键和π…π共轭作用下有规律地堆叠形成三维网络结构。配合物2是三斜晶系,Co1离子和Co1ⁱ离子由H₂L₁上的羧酸氧原子O4和O4ⁱ连接,形成双齿螯合的配位结构单元,以Co²⁺配位连接 L^2-₁和L₂形成二维网格结构,各层在O—H…O分子间氢键和范德瓦耳斯力作用下有规律的堆叠形成三维网络结构。配合物1和2均含有芳香杂环、羧基杂环和氮杂环,具有良好的荧光性质和热稳定性,最大发射波长分别为345 nm和333 nm。     

熔盐环境下热障涂层新材料Mg2SiO4的高温腐蚀研究

采用高温固相反应法合成了Mg2 SiO4陶瓷粉末,冷压成型后烧结成陶瓷块材.盐涂法制备V2 O5涂覆的样品,利用马弗炉在950℃空气气氛下保温不同时间.对热腐蚀后的样品进行表面形貌、截面特征的表征,并对Mg2 SiO4的高温熔盐腐蚀机制进行分析研究.结果表明:熔融的V2 O5对Mg2 SiO4陶瓷试样产生两种形式的腐蚀降解作用,即溶解-沉淀机制形成腐蚀产物Mg2 V2 O7和SiO2以及沿晶界腐蚀为主的渗透腐蚀作用.     

Er3+单掺、Er3+/Yb3+共掺杂Ca12Al14O32F2的 制备及上转换发光性质

利用高温固相法成功制备了Er~(3+)单掺、Er~(3+)/Yb~(3+)共掺杂Ca_(12)Al_(14)O_(32)F_2上转换发光样品。在980 nm激光激发下,Er~(3+)单掺和Er~(3+)/Yb~(3+)共掺杂样品均呈现出较强的绿光(528,549 nm)和较弱的红光(655 nm)发射,分别归因于Er~(3+)离子的~2H_(11/2),~4S_(3/2)→~4I_(15/2)和~4F_(9/2)→~4I_(15/2)能级跃迁。随着Er离子浓度的增加,单掺杂样品上转换发光强度先增大后减小,最佳掺杂浓度为0.8%。共掺杂Yb~(3+)后,Er~(3+)的发光强度明显增大。还原气氛下合成的样品上转换发光强度增大约两倍,可能和笼中阴离子基团变化有关。发光强度和激发光功率的关系表明所得上转换发射为双光子吸收过程,借助Er~(3+)-Yb~(3+)体系能级结构详细讨论了上转换发射的跃迁机制。     

自由基浓度测定方法的再验证及其在煤化学中应用

对前人建立的标准曲线法测煤中自由基浓度进行优化,以DPPH标准样品和基准样品的二次积分面积比值为新参数,结果显示新参数标准曲线法的实测值与理论值相对误差都在5%以内;重复性、复现性实验的相对标准偏差都小于3%。将新参数标准曲线法用于分析不同煤化程度煤和新疆黑山煤(HS)沥青质的自由基浓度,发现随着煤化程度增加,其煤中自由基浓度逐渐增大,从低阶褐煤的8.531×10~(17)/g上升到高阶无烟煤3.37899×10~(19)/g;而在HS煤液化过程中,随着加氢液化温度的升高,其沥青质自由基浓度逐渐下降,从290℃的1.5793×10~(18)/g降到450℃的7.410×10~(17)/g,沥青质自由基浓度变化趋势与其产率变化趋势相一致。     

棒状PANI/TiO2纳米复合材料的制备及光催化性能研究

通过共混法和原位氧化聚合法成功制备了棒状聚苯胺/TiO2纳米复合材料,通过SEM、XRD、FT-IR、TGA、TEM、紫外-可见漫反射光谱等测试对其进行表征.并以罗丹明B溶液为模拟污染物,在可见光条件下,棒状PANI/TiO2纳米复合材料的催化降解效率与纯PANI和TiO2相比明显提高.另外,对两种不同方法合成的PANI/TiO2纳米复合材料的光催化性能进行对比,结果表明原位氧化聚合法制得的复合材料,由于TiO2在复合材料中的均匀分布及其与PANI的协同效应,光催化降解率可达91.11;.     

大范围ReS2纳米带的化学气相沉积制备及特性表征

采用化学气相沉积方法,在整个SiO2(300 nm)/Si衬底上制备出了大面积、高质量的单层及多层ReS2纳米带,纳米带的长度可达150μm.利用光镜、原子力显微镜(AFM)、荧光(PL),拉曼(Raman)以及X射线光电子能谱分析(XPS)等手段对所得不同层数的ReS2样品进行了表征.结果表明:所制备的ReS2纳米带的拉曼信号与化学气相沉积方法制备的(CVD)单层及多层的薄膜材料差别不大,而其荧光峰出现了明显的展宽,且峰位出现了明显的蓝移.化学气相沉积法(CVD)制备ReS2纳米带操作简单,可控性与可重复性高,对其基础研究和未来潜在应用有着比较重要的现实意义.